A self-sacrifice template strategy to synthesize Co-LDH/MXene for lithium-ion batteries.

To overcome the limitations of both LDHs and MXenes, we develop a self-sacrifice template strategy using a zeolite imidazolate framework-67 (ZIF-67) to derive Co-LDH anchored on an MXene conductive substrate (Co-LDH/MXene). In this process, ZIF-67 grows on the MXene nanosheets, then spontaneously transforms into Co-LDH/MXene in aqueous solution at room temperature. As the LIB anode, it shows a reversible capacity of 854.

Effects of Chemical Compositions on Plating Characteristics of Alkaline Non-Cyanide Electrogalvanized Coatings.

The effects of zinc and sodium hydroxide concentrations in an alkaline non-cyanide zinc bath on the electrodeposition characteristics of zinc deposits are systematically investigated. Using microstructural and phase analyses of specimens with specifically designed geometries, the study indicates that the bath formulations critically control the electrogalvanizing characteristics and affect the coating surface morphology, deposition rate, throwing power, coating uniformity, and residual stresses developed during and after electrogalvanizing. The coatings produced from baths with a moderate Zn-to-NaOH ratio of 0.