Neurons convert external stimuli into action potentials, or spikes, and encode the contained information into the biological nervous system. Despite the complexity of neurons and the synaptic interactions in between, rate models are often adapted to describe neural encoding with modest success. However, it is not clear whether the firing rate, the reciprocal of the time interval between spikes, is sufficient to capture the essential features for the neuronal dynamics.

Structural and nanomechanical properties of BiFeO3 thin films deposited by radio frequency magnetron sputtering.

The nanomechanical properties of BiFeO3 (BFO) thin films are subjected to nanoindentation evaluation. BFO thin films are grown on the Pt/Ti/SiO2/Si substrates by using radio frequency magnetron sputtering with various deposition temperatures. The structure was analyzed by X-ray diffraction, and the results confirmed the presence of BFO phases.

Sputter-prepared (001) BiFeO3 thin films with ferromagnetic L10-FePt(001) electrode on glass substrates.

Highly textured BiFeO3(001) films were formed on L10-FePt(001) bottom electrodes on glass substrates by sputtering at reduced temperature of 400°C. Good electric polarization 2Pr = 80 and 95 μC/cm2, comparable to that of the reported epitaxial films, and coercivity Ec = 415 and 435 kV/cm are achieved in the samples with 20-nm- and 30-nm-thick electrodes. The BiFeO3(001) films show different degrees of compressive strain.