Polyelectrolyte-surfactant complex as a template for the synthesis of zeolites with intracrystalline mesopores.

Mesoporous zeolite silicalite-1 and Al-ZSM-5 with intracrystalline mesopores were synthesized with polyelectrolyte-surfactant complex as the template. Complex colloids were first formed by self-assembly of the anionic polymer poly(acrylic acid) (PAA) and the cationic surfactant cetyltrimethylammonium bromide (CTAB) in basic solution. During the synthesis procedure, upon the addition of the silica source, microporous template (tetrapropylammonium hydroxide), and NaCl, these PAA/CTA complex colloids underwent dissociation and gave rise to the formation of hollow silica spheres with mesoporous shells templated by CTAB micelles and PAA domains as the core.

Synthesis of hydrothermally stable, hierarchically mesoporous aluminosilicate Al-SBA-1 and their catalytic properties.

Hydrothermally stable mesoporous aluminosilicates Al-SBA-1 with hierarchical pore structure have been successfully synthesized under alkaline condition at 120 °C by employing organic mesomorphous complexes of polyelectrolyte (poly(acrylic acid) (PAA)) and cationic surfactant (hexadecyl pyridinium chloride (CPC)) as template. The Si/Al ratio could be as high as 5 and the incorporation of Al into the silica framework did not disturb the well-ordered cubic Pm ̅3n mesostructure. Meanwhile, the incorporation of Al could greatly increase the specific surface area and pore volume of the samples.

Facile fabrication of noble metal nanoparticles encapsulated in hollow silica with radially oriented mesopores: multiple roles of the N-lauroylsarcosine sodium surfactant.

A facile one-pot method was reported to fabricate noble metal nanoparticles encapsulated in silica hollow nanospheres with radially oriented mesopores, and the anionic amino acid surfactant, N-lauroylsarcosine sodium, played multiple roles: reducing agent, stabilizer, emulsion droplets and mesopore template.

A comparison study between polymeric ligand and monomeric ligand for oligopeptide adsorption.

This work aimed to compare two types of affinity ligands, i.e. polymeric and monomeric ligands, by investigating their adsorption affinity, capacity and selectivity to oligopeptide.

Effects of oligopeptide's conformational changes on its adsorption.

We report the effects of peptide adsorption to cross-linked polymers (adsorbents) by its conformational changes. Two adsorbents, APhe and ALeu, were prepared and expected to show high affinity to the oligopeptide VW-8 (NH(2)-Val-Val-Arg-Gly-Cys-Thr-Trp-Trp-COOH) according to our previous studies. These absorbents bared the residues of phenylalanine and leucine, respectively, and carried both hydrophobic and electrical groups.

Porous lanthanide oxides via a precursor method: morphology control through competitive interaction of lanthanide cations with oxalate anions and amino acids.

Porous lanthanide oxides were fabricated by a precursor-thermolysis method. The precursors were synthesized by a hydrothermal reaction with lanthanide (La, Ce, Pr and Nd) salts, sodium oxalate and asparagine (or glutamine). Under hydrothermal conditions asparagine and glutamine exhibited greatly different complexation abilities with lanthanide cations.

Effect of alcohol on morphology and mesostructure control of anionic-surfactant-templated mesoporous silica (AMS).

In the synthesis of anionic-surfactant-templated mesoporous silica (AMS), the effects of alcohols have been investigated for the first time. Without the addition of extra alcohols, spherical mesoporous silica with radially oriented mesopores could be obtained through the anionic surfactant templating route. By using alcohols with different carbon chain length such as ethanol, n-butanol, hexanol and 1-octanol as the additives, different morphologies and mesostructures of mesoporous silica were obtained.

Anionic surfactant-templated mesoporous silica (AMS) nano-spheres with radially oriented mesopores.

Mesoporous silica nano-spheres with pore size larger than 3 nm were synthesized using an anionic surfactant as the template. These nano-spheres possess centrosymmetric radial mesopores (emanating from the spherical center to the exterior surface) and form stable suspension. The spherical size and mesostructure can be finely tuned by changing the pH value of the synthetic system in the range of 8.