Synthesis of 3D Dendritic Gold Nanostructures Assisted by a Templated Growth Process: Application to the Detection of Traces of Molecules.

Complex architectures like 3D gold dendritic nanostructures were synthesized by an templated growth method using a thin film of a block copolymer [polystyrene--poly(4-vinylpyridine)] deposited onto silicon substrates. The overall study has demonstrated the strong link between the morphology, size, and distribution of the structures and the synthetic physicochemical parameters, such as pH, reaction temperature, concentration, and nature of reactants. A nonequilibirum state of the medium has been required to create a fractal growth of the gold structures onto a prepatterned gold-seeded surface and has led to a better control of the structures' surface coverage rate.

How do titanium and Ti6Al4V corrode in fluoridated medium as found in the oral cavity? An in vitro study.

The purpose of this work was to evaluate the corrosion of commercially pure (CP) titanium and Ti6Al4V in vitro at different F(-) concentrations regularly found in the oral cavity by using different electrochemical tests and surface analysis techniques. electrochemical impedance spectroscopy (EIS), open circuit potential (OCP) and potentiodynamic polarization tests were associated to advanced characterization techniques such as SEM, EDS, AFM, ICP-MS and XPS. OCP tests revealed a higher reactivity of both CP titanium and Ti6Al4V at 12,300 ppm F(-) concentration than that recorded at 227 ppm F(-).

Initial sliding wear kinetics of two types of glass ionomer cement: a tribological study.

The aim of this work was to characterize the initial wear kinetics of two different types of glass ionomer cement used in dentistry (the conventional glass ionomer cement and the resin-modified glass ionomer cement) under sliding friction after 28-day storing in distilled water or Ringer's solution. Sliding friction was applied through a pin-on-disk tribometer, in sphere-on-plane contact conditions, under 5 N normal load and 120 rotations per minute. The test lasted 7500 cycles and replicas were performed at 2500, 5000 and 7500 cycles.

Corrosion behaviour of titanium in the presence of Streptococcus mutans.

Objective: The main aim of this in vitro study was to evaluate the influence of Streptococcus mutans on the corrosion of titanium.

Methods: S. mutans biofilms were formed on commercially pure titanium (CP-Ti) square samples (10mm×10mm×1mm) using a culture medium enriched with sucrose.

Impedance methodology: A new way to characterize the setting reaction of dental cements.

Objectives: Impedance spectroscopy is a non-destructive, quantitative method, commonly used nowadays for industrial research on cement and concrete. The aim of this study is to investigate the interest of impedance spectroscopy in the characterization of setting process of dental cements.

Methods: Two types of dental cements are used in this experiment: a new Calcium Silicate cement Biodentine™ (Septodont, Saint Maur-des Fossés, France) and a glass ionomer cement resin modified or not (Fuji II(®) LC Improved Capsules and Fuji IX(®) GP Fast set Capsules, GC Corp.