Magnetic field-dependent spin structures of nanocrystalline holmium.

The results are reported of magnetic field-dependent neutron diffraction experiments on polycrystalline inert-gas condensed holmium with a nanometre crystallite size ( = 33 nm). At = 50 K, no evidence is found for the existence of helifan(3/2) or helifan(2) structures for the nanocrystalline sample, in contrast with results reported in the literature for the single crystal. Instead, when the applied field is increased, the helix pattern transforms progressively, most likely into a fan structure.

Magnetic coupling mechanisms in particle/thin film composite systems.

Magnetic γ-Fe(2)O(3) nanoparticles with a mean diameter of 20 nm and size distribution of 7% were chemically synthesized and spin-coated on top of a Si-substrate. As a result, the particles self-assembled into a monolayer with hexagonal close-packed order. Subsequently, the nanoparticle array was coated with a Co layer of 20 nm thickness.