Influence of Heat Treatment Temperature on Microstructure, Hardness and Sensitization of UNS S32205 Duplex Stainless Steel.

Improper thermal cycles on duplex stainless steels can lead to the formation of detrimental phases or alter the proportion of ferrite and austenite phases, thus influencing the material's mechanical properties and corrosion resistance. Therefore, this study aimed to evaluate the effect of aging (at 850 and 950 °C) and solubilization (at 1000 and 1150 °C) thermal treatments on microstructure, indentation hardness, elasticity modulus, and susceptibility to intergranular corrosion of UNS S32205 duplex stainless steel. The sigma phase (σ) formation in the aged samples, with hardness values between 8 and 10 GPa, was confirmed.