Printed circuit board substrates derived from lignocellulose nanofibrils for sustainable electronics applications.

This study investigates lignocellulose nanofibrils (LCNF) as a sustainable alternative material for printed circuit board (PCB) substrates, demonstrating an application through the development of an eco-friendly computer mouse demonstrator. LCNF is derived from lignin-rich cellulose pulp, a side stream product of biorefinery processes, combining the natural strength of cellulose fibrils with lignin to enhance mechanical and electrochemical properties. The research outlines the process of fibrillating lignin-rich cellulose pulp at 10 kW/h per kg into LCNF, followed by thermal and pressure treatment (at Δp = 50 - 1500 kN, ΔT = 30 - 120 °C) to achieve a rigid PCB substrate.

Optical Polymer Waveguides Fabricated by Roll-to-Plate Nanoimprinting Technique.

The paper reports on the properties of UV-curable inorganic-organic hybrid polymer multimode optical channel waveguides fabricated by roll-to-plate (R2P) nanoimprinting. We measured transmission spectra, refractive indices of the applied polymer materials, and optimized the R2P fabrication process. Optical losses of the waveguides were measured by the cut-back method at wavelengths of 532, 650, 850, 1310, and 1550 nm.

Gas sensing properties of nanocrystalline diamond at room temperature.

This study describes an integrated NH3 sensor based on a hydrogenated nanocrystalline diamond (NCD)-sensitive layer coated on an interdigitated electrode structure. The gas sensing properties of the sensor structure were examined using a reducing gas (NH3) at room temperature and were found to be dependent on the electrode arrangement. A pronounced response of the sensor, which was comprised of dense electrode arrays (of 50 µm separation distance), was observed.