Microstructure-dependent crevice corrosion damage of implant materials CoCr28Mo6, TiAl6V4 and REX 734 under severe inflammatory conditions.

Fretting corrosion is associated with increased risk of premature implant failure. In this complex in vivo corrosion system, the contribution of static crevice corrosion of the joined metal alloys is still unknown. The aim of this study was to develop a methodology for testing crevice corrosion behavior that simulates the physiological conditions of modular taper junctions and to identify critical factors on corrosion susceptibility.