Pressure Induced Densification and Compression in a Reprocessed Borosilicate Glass.

Pressure induced densification and compression of a reprocessed sample of borosilicate glass has been studied by X-ray radiography and energy dispersive X-ray diffraction using a Paris-Edinburgh (PE) press at a synchrotron X-ray source. The reprocessing of a commercial borosilicate glass was carried out by cyclical melting and cooling. Gold foil pressure markers were used to obtain the sample pressure by X-ray diffraction using its known equation of state, while X-ray radiography provided a direct measure of the sample volume at high pressure.

Effect of Loading Rate Upon Conventional Ceramic Microindentation Hardness.

The world standards for conventional ceramic hardness have varying requirements for control of loading rate during the indentation cycle. A literature review suggests that loading rate may affect measured hardness in some instances. In view of the uncertainty over this issue, new experiments over a range of indentation loading rates were performed on a steel, sintered silicon carbide, and an aluminum oxynitride.