Viscoplastic crack initiation and propagation in crosslinked UHMWPE from clinically relevant notches up to 0.5mm radius.

Highly crosslinked UHMWPE is now the material of choice for hard-on-soft bearing couples in total joint replacements. However, the fracture resistance of the polymer remains a design concern for increased longevity of the components in vivo. Fracture research utilizing the traditional linear elastic fracture mechanics (LEFM) or elastic plastic fracture mechanics (EPFM) approach has not yielded a definite failure criterion for UHMWPE.

Application of viscoelastic fracture model and non-uniform crack initiation at clinically relevant notches in crosslinked UHMWPE.

The mechanism of crack initiation from a clinically relevant notch is not well-understood for crosslinked ultra high molecular weight polyethylene (UHMWPE) used in total joint replacement components. Static mode driving forces, rather than the cyclic mode conditions typically associated with fatigue processes, have been shown to drive crack propagation in this material. Thus, in this study, crack initiation in a notched specimen under a static load was investigated.

An elaborate data set characterizing the mechanical response of the foot.

Mechanical properties of the foot are responsible for its normal function and play a role in various clinical problems. Specifically, we are interested in quantification of foot mechanical properties to assist the development of computational models for movement analysis and detailed simulations of tissue deformation. Current available data are specific to a foot region and the loading scenarios are limited to a single direction.