Effect of Exposure Conditions on Mortar Subjected to an External Sulfate Attack.

This study aims to investigate the influence of exposure conditions on the behavior of mortar subjected to an external sulfate attack (ESA). Three different exposure conditions (full immersion, semi-immersion, and drying/wetting cycles) were tested on mortar prisms made with Portland cement and two w/c ratios (0.45 and 0.

Effect of an Early-Age Exposure on the Degradation Mechanisms of Cement Paste under External Sulfate Attack.

Among the most significant causes of concrete degradation is ESA (external sulfate attack). The majority of studies are currently conducted on samples that have been saturated and matured. Concrete structures, however, are exposed to the environment once the formwork has been removed.

A Critical Review of Existing Test-Methods for External Sulfate Attack.

External sulfate attack (ESA) of cementitious materials has been studied worldwide for a very long time. This physical/chemical interaction between sulfate ions and the cement hardened elements affects the long-term durability of concrete structures: cracking, spalling or strength loss of concrete structures. To study these damaging phenomena, some standardized and non-standardized accelerated aging tests are used to evaluate the performance of cements in sulfate-rich environments.