Development of oxidation-resistant and electrically conductive coating of Ti-Al-C system for the lightweight interconnects of solid oxide fuel cells.

The paper studies oxidation resistance and electrical conductivity of dense coatings produced by vacuum-arc deposition technique on α-titanium thin (0.1 mm) substrate using a hot pressed TiAlC-TiC target. The coatings were deposited at low (7 mA/cm) and high (15 mA/cm) current densities on the substrate and marked LCD and HCD, respectively.

Preconditioning of the YSZ-NiO Fuel Cell Anode in Hydrogenous Atmospheres Containing Water Vapor.

The YSZ-NiO ceramics for solid oxide fuel cells (SOFCs) anode have been investigated. A series of specimens were singly reduced in a hydrogenous atmosphere (Ar-5 vol% H mixture) at 600 °C under the pressure of 0.15 MPa or subjected to 'reduction in the mixture-oxidation in air' (redox) cycling at 600 °C.

Oxidation Resistance of Materials Based on Ti3AlC2 Nanolaminate at 600 °C in Air.

The oxidation behavior of Ti3AlC2-based materials had been investigated at 600 °C in static air for 1000 h. It was shown that the intense increase of weight gain per unit surface area for sintered material with porosity of 22 % attributed to oxidation of the outer surface of the specimen and surfaces of pores in the bulk material. The oxidation kinetics of the hot-pressed Ti3AlC2-based material with 1 % porosity remarkably increased for the first 15 h and then slowly decreased.

Influence of Treatment Temperature on Microstructure and Properties of YSZ-NiO Anode Materials.

The cyclic treatment technique (redox cycling) comprising stages of material exposition in reducing and oxidizing high-temperature environments and intermediate degassing between these stages has been developed to improve the structural integrity of YSZ-NiO ceramic anode substrates for solid oxide fuel cells. A series of specimens were singly reduced in a hydrogenous environment (the Ar-5 vol% Н2 mixture or hydrogen of 99.99 vol% H2 purity) under the pressure of 0.