Silica-supported Au nanoparticles decorated by TiO2: formation, morphology, and CO oxidation activity.

Au-TiO(2) interface on silica support was aimed to be produced in a controlled way by use of Au hydrosol. In method A, the Au colloids were modified by hydrolysis of the water-soluble Ti(IV) bis(ammoniumlactato)dihydroxide (TALH) precursor and then adsorbed on Aerosil SiO(2) surface. In method B, Au sol was first deposited onto the SiO(2) surface and then TALH was adsorbed on it.

Gold nanoparticles deposited on SiO2/Si100: correlation between size, electron structure, and activity in CO oxidation.

Nanosize gold particles were prepared by Ar(+) ion implantation of 10-nm thick gold film deposited onto a SiO(2)/Si(100) wafer possessing no catalytic activity in the CO oxidation. Along with size reduction the valence band of the gold particles and the actual size were determined by ultraviolet- and X-ray photoelectron spectroscopy (UPS, XPS) and by transmission electron microscopy (TEM) as well as atomic force microscopy (AFM), respectively. The catalytic activity was determined in the CO oxidation.