DC bias immune nanocrystalline magnetic cores made of Fe73Nb3Cu1B7Si16 ribbon with induced transverse magnetic anisotropy.

The comparative analysis of magnetic properties of cut cores made of nanocrystalline Fe73Nb3Cu1B7Si16 alloy ribbon and cores made of the same ribbon with preliminary tension-induced transverse magnetic anisotropy was carried out. The possibility of improving magnetic properties of cut cores, decreasing loss, and increasing DC bias immunity of reversible magnetic permeability is presented. The influence of induced magnetic anisotropy on DC bias immunity of reversible magnetic permeability was investigated.

Soft magnetic properties of nanocrystalline Fe73B7Si16Nb3Cu1 alloy after rapid heating under tensile stress.

Amorphous Fe73B7Si16Nb3Cu1 ribbon was crystallized rapidly by electric current heating under simultaneously applied tensile stress along the ribbon axis. As a result, strong transverse magnetic anisotropy was induced in the ribbon. Dynamic magnetic properties of the ribbons rapidly heated either under the tensile stress or without tensile stress were measured using toroidal cores.