A Microscopy Evaluation of Emergence Profile Surfaces of Dental Custom CAD-CAM Implant Abutments and Dental Implant Stock Abutments.

Recently, due to the high demand for dental implants, the use of dental implant stock abutments has increased significantly, especially dental custom CAD/CAM implant abutments milled by dental technicians in their laboratories. The purpose of this study is to analyze the surface quality of the emergence profile of dental custom CAD/CAM implant abutments made by a non-industrial milling machine, compared to original and compatible dental implant stock abutments made by industrial machines. Thirty dental implant abutments were divided into six study lots.

Stereomicroscopic Aspects of Non-Carious Cervical Lesions.

Non-carious cervical lesions (NCCLs) represent a form of tooth wear, characterized by the irreversible loss of dental hard tissues at the enamel-cement junction, without the involvement of caries and dental trauma. The aim of this study was to highlight the morphological elements of NCCLs via their stereomicroscopic examination and to confirm the role of this examination in the diagnosis of early lesions. In addition, the association between the morphological aspects identified during the stereomicroscopic examination of NCCLs and their etiological factors was determined.

Osseointegration evaluation of an experimental bone graft material based on hydroxyapatite, reinforced with titanium-based particles.

Bone graft materials are more and more frequently used in dentistry for improving the periodontal support and for creating a bone support favorable for the insertion of dental implants. The experimental study carried out on laboratory animals aimed to evaluate the biocompatibility and the manner of integration of an experimental bone augmentation material, based on hydroxyapatite (HAp), reinforced with titanium-based particles by comparison with a commercial synthetic graft material already existing on the profile market, also based on HAp. We noticed a common pattern of evolution, although there were differences related to the speed of new bone tissue formation and implicitly the morphological elements captured at the two moments of time.

Calcium fructoborate coating of titanium-hydroxyapatite implants by chemisorption deposition improves implant osseointegration in the femur of New Zealand White rabbit experimental model.

Background: The identification of biocomposites that improve cell adhesion and reduce bone integration time is a great challenge for implantology and bone reconstruction.

Aim: Our aim was to evaluate a new method of chemisorption deposition (CD) for improving the biointegration of hydroxyapatite-coated titanium (HApTi) implants. CD method was used to prepare a calcium fructoborate (CaFb) coating on a HApTi (HApTiCaFb) implant followed by evaluation of histological features related to bone healing at the interface of a bioceramic material in an animal model.

A microscopic insight of the morphological changes induced by dental zirconia prosthetic structures.

As zirconia is today probably the dental material with the largest increase in the frequency of use in dental prosthetics, the reason for this study was based on a series of clinical observations made following its use in clinical prosthetics. Thus, we were interested in two aspects: the histological evaluation of the response of the oral soft tissues to the presence of the prosthetic structures in zirconia, and the microscopic evaluation of the abrasion lesions that appeared in the hard dental tissues of the zirconia prostheses antagonists. For the first part, samples from three zirconia-based dental prosthetics commercial products were implanted submucosal in the oral cavity of male Wistar rats.

A correlation between thermodynamic properties, thermal expansion and electrical resistivity of Ag-28% Cu nanopowders processed by the mechanical alloying route.

Thermodynamic properties, thermal expansion and electrical resistivity of the Ag-28% Cu nanopowders processed by the mechanical alloying route have been investigated in the temperature range from ambient to 1048 K. The thermodynamic properties represented by the relative enthalpy, the specific heat capacity, the relative entropy and the Gibbs energy function obtained from drop calorimetric measurements have been used to reveal the occurrence of the micro-relaxation process, as well as of the correlative effects of decomposition and growth processes. On the basis of the results, the parameters that favour stable nanostructured systems in Ag-28% Cu powders synthesized by the mechanical alloying route have been identified.