Structural transitions of epitaxial ceria films on Si(111).

The structural changes of a (111) oriented CeO2 film grown on a Si(111) substrate covered with a hex-Pr2O3(0001) interface layer due to post deposition annealing are investigated. X-ray photoelectron spectroscopy measurements revealing the near surface stoichiometry show that the film reduces continuously upon extended heat treatment. The film is not homogeneously reduced since several coexisting crystalline ceria phases are stabilized due to subsequent annealing at different temperatures as revealed by high resolution low energy electron diffraction and X-ray diffraction.