Light-induced high-spin state in ZnO nanoparticles.

The effects of white-light irradiation on ∼15 nm diameter ZnO nanoparticles are investigated by means of electron paramagnetic resonance, near liquid-nitrogen and liquid-helium temperatures. Under dark conditions, usual core- and surface-defects are detected, respectively, at g = 1.960 and g = 2.

Core-defect reduction in ZnO nanorods by cobalt incorporation.

Zinc oxide (ZnO) nanorods grown by the low-temperature (90 °C) aqueous chemical method with different cobalt concentration within the synthesis solution (from 0% to 15%), are studied by electron paramagnetic resonance (EPR), just above the liquid helium temperature. The anisotropic spectra of substitutional Co reveal a high crystalline quality and orientation of the NRs, as well as the probable presence of a secondary disordered phase of ZnO:Co. The analysis of the EPR spectra indicates that the disappearance of the paramagnetic native core-defect (CD) at [Formula: see text] is correlated with the apparition of the Co ions lines, suggesting a gradual neutralization of the former by the latter.