Vaporization Mechanisms of Water-Insoluble Cs in Ash During Thermal Treatment with Calcium Chloride Addition.

The vaporization mechanisms of water-insoluble Cs in raw ash and Cs-doped ash during thermal treatment with CaCl addition was systematically examined in a lab-scale electrical heating furnace over a temperature range of 500-1500 °C. The results indicate that the water-insoluble Cs in the ash was associated with aluminosilicate as pollucite. Addition of 10% CaCl caused the maximum vaporization ratio of Cs in the raw ash to reach approximately 80% at temperatures higher than 1200 °C, whereas approximately 95% of Cs was vaporized at temperatures higher than 1300 °C when 30% CaCl was added.