Improving Environmental Stress Cracking Resistance of High-Density Polyethylene Grades by Comonomer Addition and Nanocomposite Approach.

The aim of this paper is to determine the effect of polymer density, correlated to the comonomer content, and nanosilica addition on the mechanical and Environmental Stress Cracking Resistance (ESCR) characteristics of high-density polyethylene (HDPE). In this regard, five HDPE samples with similar Melt Flow Index (MFI) and molar mass but various densities were acquired from a petrochemical plant. Two polymerization reactors work in series and differ only in the amount of 1-buene comonomer fed to the second reactor.

Silyl diol ester as a new selectivity control agent in MgCl-supported Ziegler-Natta systems for propylene polymerization: catalyst structure and polymer properties.

In this study, bis(benzoyloxy)dimethylsilane (SDE) was developed as a non-phthalate selectivity control agent (internal donor (ID) and external donor (ED)) in MgCl-supported Ziegler-Natta (ZN) systems. The impact of SDE as an ID was investigated in regards to chemical composition, morphology, adsorption behavior (using FTIR spectroscopy, WAXD and SEM studies) and the propylene polymerization performance of the catalyst. The results of the adsorption behavior of SDE revealed that SDE, while able to stabilize the electronically unsaturated surfaces of MgCl [(104) and (110)], has a rather high tendency to be absorbed on strongly acidic Mg ions at the corners of these crystals.