Effect of Hydrothermal, Chemical, and Mechanical Degradation on Flexural Strength and Phase Transformation of Ground, Glazed, and Polished Zirconia.

Evaluation of the effect of grinding on flexural strength of zirconia after low temperature degradation (LTD) and pH-cycling. Sixty-four bar-shaped specimens of yttria-stabilized tetragonal polycrystalline zirconia were milled, sintered, wet-polished, and divided into 8 groups (N=8). The four control groups were not aged while artificial aging was performed in the 4 experimental groups in three steps including LTD in steam for 40h, pH-cycling, and tooth brushing for artificial aging.

Effect of Low-Temperature Degradation, Ph-Cycling and Simulated Tooth Brushing on Surface Roughness, Topography, and Polish Retention of Yttrium-Stabilized Tetragonal Zirconia.

Statement Of The Problem: Surface roughness of zirconia is an important parameter that determines the success of zirconia restorations. When zirconia surfaces are left rough, higher susceptibility to hydrothermal aging, plaque accumulation and color changes would occur. Therefore, polish retention of these restorations is considered as a challenge.