Integrating two-dimensional (2D) layered materials with wide bandgap β-GaO has unveiled impressive opportunities for exploring novel physics and device concepts. This study presents the epitaxial growth of 2D β-InSe/3D β-GaO heterostructures on c-Sapphire substrates by plasma-assisted molecular beam epitaxy. Firstly, we employed a temperature-dependent two-step growth process to deposit GaO and obtained a phase-pure β-GaO film on c-Sapphire.
View Article and Find Full Text PDFHydrostatically pressurized studies using diamond anvil cells on the structural phase transition of the free-standing screw-dislocation-driven (SDD) GaSe thin film synthesized by molecular beam epitaxy have been demonstrated via in-situ angle-dispersive synchrotron X-ray diffraction and Raman spectroscopy. The early pressure-driven hexagonal-to-rock salt transition at approximately ~ 20 GPa as well as the outstandingly structural-phase memory after depressurization in the SDD-GaSe film was recognized, attributed to the screw dislocation-assisted mechanism. Note that, the reversible pressure-induced structural transition was not evidenced from the GaSe bulk, which has a layer-by-layer stacking structure.
View Article and Find Full Text PDFTwo-dimensional (2D) layered GaSe films were grown on GaAs (001), GaN/Sapphire, and Mica substrates by molecular beam epitaxy (MBE). The in situ reflective high-energy electron diffraction monitoring reveals randomly in-plane orientations of nucleated GaSe layers grown on hexagonal GaN/Sapphire and Mica substrates, whereas single-orientation GaSe domain is predominant in the GaSe/GaAs (001) sample. Strong red-shifts in the frequency of in-plane [Formula: see text] vibration modes and bound exciton emissions observed from Raman scattering and photoluminescence spectra in all samples are attributed to the unintentionally biaxial in-plane tensile strains, induced by the dissimilarity of symmetrical surface structure between the 2D-GaSe layers and the substrates during the epitaxial growth.
View Article and Find Full Text PDFRegardless of the dissimilarity in the crystal symmetry, the two-dimensional GaSe materials grown on GaAs(001) substrates by molecular beam epitaxy reveal a screw-dislocation-driven growth mechanism. The spiral-pyramidal structure of GaSe multi-layers was typically observed with the majority in ε-phase. Comprehensive investigations on temperature-dependent photoluminescence, Raman scattering, and X-ray diffraction indicated that the structure has been suffered an amount of strain, resulted from the screw-dislocation-driven growth mechanism as well as the stacking disorders between monolayer at the boundaries of the GaSe nanoflakes.
View Article and Find Full Text PDF© LitMetric 2025. All rights reserved.