Coating based on chitosan/vancomycin nanoparticles: Patterns of formation in a water-carbon dioxide biphase system and in vivo stability.

The patterns of formation of chitosan nanoparticles doped with vancomycin and coatings based on them in carbonate solutions have been investigated for the first time in this study. Using a technique of radioactive indicators, it was found that at a CO pressure of 30 MPa, the yield of the nanoparticles was ∼85 %, and a maximum antibiotic encapsulation efficiency of ∼30 % was achieved. By spectrophotometric and high-resolution microscopy, it was found that the coating of stabilized xenopericardial tissue of bioprosthetic heart valve, based on chitosan nanoparticles doped with vancomycin with a zeta potential |ζ| ∼20 mV completely covers collagen fibers by depositing about 60 nm nanoparticles onto them under direct deposition from carbonic acid at a pressure of 30 MPa CO.

Hydrophilization and Functionalization of Fullerene C with Maleic Acid Copolymers by Forming a Non-Covalent Complex.

In this study, we report an easy approach for the production of aqueous dispersions of C fullerene with good stability. Maleic acid copolymers, poly(styrene--maleic acid) (SM), poly(N-vinyl-2-pyrrolidone--maleic acid) (VM) and poly(ethylene--maleic acid) (EM) were used to stabilize C fullerene molecules in an aqueous environment by forming non-covalent complexes. Polymer conjugates were prepared by mixing a solution of fullerene in N-methylpyrrolidone (NMP) with an aqueous solution of the copolymer, followed by exhaustive dialysis against water.

Chitosan/hyaluronic acid polyanion bilayer applied from carbon acid as an advanced coating with intelligent antimicrobial properties for improved biological prosthetic heart valves.

The tightly bonded shielding coating on biomatrix significantly enhances the functionality of medical devices, bioprostheses in particular. In our work we have obtained a polyelectrolyte coating on a biomatrix by sequentially depositing chitosan and hyaluronic acid (HA) from solutions in carbonic acid under pressure. This approach makes it possible to obtain hybrid biomatrix with a firmly bonded polymer screen due to the electrostatic bonding of polyions.