Compressive strength and fluoride release profile of a glass ionomer cement reinforced with silver-hydroxyapatite-silica hybrid nanoparticles: An in vitro study.

Objectives: This study aimed to prepare a glass ionomer (GI) cement reinforced with silver-hydroxyapatite-silica (Ag/HA/Si) hybrid nanoparticles and assess its compressive strength and fluoride release profile.

Material And Methods: In this in vitro, experimental study, 60 cylindrical specimens were fabricated with 4mm diameter and 6mm height in 6 groups (n=10) using BracePaste composite, GC Fuji II LC pure RMGI, and RMGI reinforced with 0.1wt%, 0.

Effect of incorporating silica-hydroxyapatite-silver hybrid nanoparticles into the resin-modified glass ionomer on the adhesive remnant index score and shear bond strength of orthodontic metal brackets: An in vitro study.

Objectives: This study aimed to assess the effect of addition of silica-hydroxyapatite-silver (Si-HA-Ag) hybrid nanoparticles to light-cure glass ionomer (GI) on shear bond strength (SBS) of metal brackets bonded with this adhesive and the adhesive remnant index (ARI) score.

Material And Methods: In this in vitro experimental study, 50 sound extracted premolars were assigned to 5 groups (n=10) for orthodontic metal bracket bonding with BracePaste® composite, Fuji ORTHO™ pure resin modified GI (RMGI), and RMGI reinforced with 2wt%, 5wt% and 10wt% Si-HA-Ag nanoparticles. The SBS of brackets was measured by a universal testing machine.