Influence of Aging and Surface Treatment on the Composite Bond Strength to Translucent 3Y-TZP Zirconia.

Purpose: The purpose of this study was to assess the effect of aging and alumina-particle air abrasion at different pressures on the bond strength of two luting composites to a translucent 3Y-TZP zirconia.

Materials And Methods: Half of the 192 disk-shaped zirconia specimens were aged in an autoclave (group A) for 20 h (134°C, 2 bar), and the other half was not aged (group N). For each group, a different surface treatment was applied: as-sintered (group SIN), alumina-particle air abrasion either at 1 bar (group 1B) or at 2.

Influence of Aging on Biaxial Flexural Strength and Hardness of Translucent 3Y-TZP.

The purpose of this research was to evaluate the influence of aging and surface treatment on surface roughness, biaxial flexural strength (BFS), and Vickers hardness (VHN) of translucent dental zirconia. Half of 80 disc-shaped zirconia specimens (1.2 mm thickness and 12 mm diameter) were aged (group A) in an autoclave for 20 h (134 °C and 0.