Preparation and characterization of the ferroelectric potassium nitrate: poly(vinyl alcohol) composite films.

The composite films of ferroelectric potassium nitrate (KNO3):poly(vinyl alcohol) (PVA) with different weight percentages of KNO3 have been prepared at 200 degrees C using the spray-deposition technique. The remanent polarization (Pr) and peak current density for all composite films was estimated by tracing the polarization-electric field (P-E) hysteresis loop and current density-electric field (J-E) loop, respectively, using a modified Sawyer-Tower circuit. Pure KNO3 is known not to exhibit any ferroelectricity under ambient conditions, but the X-ray diffraction (XRD) studies of PVA:KNO3 composite films reveal the presence of a ferroelectric phase III of KNO3 in the composite films at room temperature.