Comparison of polymerization stresses of dental resin composites evaluated by two indentation fracture methods.

Background: Polymerization stress is a major problem in dental resin composite restorations. Two indentation fracture methods can be applied to evaluate the stress, however, they often calculate different values.

Objective: To compare polymerization stresses of dental composites determined by the two methods.

Changes of residual stresses on the surface of leucite-reinforced ceramic restoration luted with resin composite cements during aging in water.

The objective of this study was to compare the changes in the residual stresses present on the surface of leucite-reinforced dental ceramic restorations luted with a self-adhesive and a conventional resin composite cement during aging in water. Ring specimens made of a leucite-reinforced ceramics were luted to ceramic cylinders using a self-adhesive (Panavia SA Luting Plus) or a conventional resin composite cement (Panavia V5) in dual-cure or self-cure mode. Residual stresses on the ring surface were measured using indentation fracture method at 1 h, 1, 3, 7, 14 and 28 days of the 37 °C water immersion.

Residual polymerization stresses in human premolars generated with Class II composite restorations.

The objective of this study was to assess the influence of filling techniques on residual polymerization stresses in resin composite restorations of the tooth. Flat planes were ground in buccal enamel surfaces of extracted human premolars, followed by preparing Class II cavities. Indentation cracks were introduced in the planes and crack lengths were measured mesio-distally (x-direction) and cervico-incisally (y-direction).