Effect of silane and MDP-based primers on physico-chemical properties of zirconia and its bond strength to resin cement.

Objective: To evaluate the effect of surface treatments on yttria-tetragonal zirconia polycrystal (Y-TZP) characteristics and on resin-mediated zirconia bond.

Methods: Y-TZP slabs were grit blasted with 45μm alumina or with 30μm silica-coated alumina particles. The chemical treatments were: no-chemical treatment (NC), silane-containing primer (SP), MDP (10-Methacryloyloxydecyl dihydrogen phosphate) and silane-containing primer (MPS), MDP-containing primer (MP) and MDP and silane-containing adhesive (MPA).

Simulated occlusal adjustments and their effects on zirconia and antagonist artificial enamel.

Purpose: The aim of this study was to evaluate the effect of occlusal adjustments on the surface roughness of yttria-tetragonal zirconia polycrystal (Y-TZP) and wear of opposing artificial enamel.

Materials And Methods: Twenty-five Y-TZP slabs from each brand (Lava, 3M and Bruxzir, Glidewell Laboratories) with different surface conditions (Control polished - CPZ; Polished/ground - GRZ; Polished/ground/repolished - RPZ; Glazed - GZ; Porcelain-veneered - PVZ; n=5) were abraded (500,000 cycles, 80 N) against artificial enamel (6 mm diameter steatite). Y-TZP roughness (in µm) before and after chewing simulation (CS) and antagonist steatite volume loss (in mm) were evaluated using a contact surface profilometer.