Effect of Hyaluronic Acid on the Activity of Methylene Blue in Photogeneration of O.

The effect of a natural polysaccharide (hyaluronic acid (HA)) on the photocatalytic activity of methylene blue (MB) was studied both under model conditions (a tryptophan photooxidation reaction in water) and with in vitro experiments on and bacterial cultures. It was shown spectrophotometrically that, in the presence of HA, an increase in the optical density of the absorption bands λ = 665 nm and 620 nm-which correspond to the monomeric and dimeric forms of the dye, respectively-was observed in the EAS of the dye, while the ratio of the optical density of these bands remained practically unchanged. When adding HA to MB, the intensity of singlet oxygen O photoluminescence and the degree of fluorescence polarization of MB increase.

Methylene Blue Solid Alginate Gels for Photodynamic Therapy: The Peculiarities of Production and Controlled Release of the Dye.

The purpose of this work is to establish the influence of the nature of solid alginate gels (alginic acid, AAG; calcium alginate, CAG) and the conditions of methylene blue (MB) introduction to alginate matrices upon its release into aqueous media. MB is an active photosensitizer, which is used in the photodynamic therapy of tumors and purulent wounds. Solid alginate gels based on AAG and CAG were obtained by adding hydrochloric acid and calcium chloride to sodium alginate.

Preparation and characterization of poly(3-hydroxybutyrate)/chitosan composite films using acetic acid as a solvent.

Poly(3-hydroxybutyrate) and chitosan are among the most widely used polymers for biomedical applications due to their biocompatibility, renewability and low toxicity. The creation of composite materials based on biopolymers belonging to different classes makes it possible to overcome the disadvantages of each of the components and to obtain a material with specific properties. Solving this problem is associated with difficulties in the selection of conditions and solvents for obtaining the composite material.

Composite Hydrogels Based on Cross-Linked Chitosan and Low Molecular Weight Hyaluronic Acid for Tissue Engineering.

The objectives of the study were as follows: (1) to develop two methods for the preparation of macroporous composite chitosan/hyaluronic acid (Ch/HA) hydrogels based on covalently cross-linked Ch and low molecular weight (Mw) HA (5 and 30 kDa); (2) to investigate some properties (swelling and in vitro degradation) and structures of the hydrogels; (3) to evaluate the hydrogels in vitro as potential biodegradable matrices for tissue engineering. Chitosan was cross-linked with either genipin (Gen) or glutaraldehyde (GA). Method 1 allowed the distribution of HA macromolecules within the hydrogel (bulk modification).

Effect of Chitosan and Amphiphilic Polymers on the Photosensitizing and Spectral Properties of Rose Bengal.

The influence of chitosan (CS) and amphiphilic polymers (AP: pluronic F108 and polyvinylpyrrolidone (PVP)) on the photocatalytic activity of rose bengal (RB) in a model reaction of tryptophan photo-oxidation in phosphate-buffered saline (PBS) was studied. It was shown that in the presence of CS, the effective rate constant of tryptophan photo-oxidation catalyzed by RB in PBS solution decreases by a factor of two. This is due to the ionic interaction of the RB with the chitosan.