In vivo resorption of injectable apatitic calcium phosphate cements: Critical role of the intergranular microstructure.

The in vivo resorption rate of two injectable apatitic calcium phosphate cements used in clinics (Graftys® HBS and NORIAN®) was compared, using a good laboratory practice (GLP) study based on an animal model of critical-sized bone defect. To rationalize the markedly different biological properties observed for both cements, key physical features were investigated, including permeability and water-accessible porosity, total porosity measured by mercury intrusion and gravimetry, and microstructure. Due to a different concept for creating porosity between the two cements investigated in this study, a markedly different microstructural arrangement of apatite crystals was observed in the intergranular space, which was found to significantly influence both the mechanical strength and in vivo degradation of the two calcium phosphate cements.

Design and properties of a novel radiopaque injectable apatitic calcium phosphate cement, suitable for image-guided implantation.

An injectable purely apatitic calcium phosphate cement (CPC) was successfully combined to a water-soluble radiopaque agent (i.e., Xenetix ), to result in an optimized composition that was found to be as satisfactory as poly(methyl methacrylate) (PMMA) formulations used for vertebroplasty, in terms of radiopacity, texture and injectability.

A straightforward approach to enhance the textural, mechanical and biological properties of injectable calcium phosphate apatitic cements (CPCs): CPC/blood composites, a comprehensive study.

Unlabelled: Two commercial formulations of apatitic calcium phosphate cements (CPCs), Graftys® Quickset (QS) and Graftys® HBS (HBS), similar in composition but with different initial setting time (7 and 15min, respectively), were combined to ovine whole blood. Surprisingly, although a very cohesive paste was obtained after a few minutes, the setting time of the HBS/blood composite dramatically delayed when compared to its QS analogue and the two blood-free references. Using solid state NMR, scanning electron microscopy and high frequency impedance measurements, it was shown that, in the particular case of the HBS/blood composite, formation of a reticulated and porous organic network occurred in the intergranular space, prior to the precipitation of apatite crystals driven by the cement setting process.