High temperature corrosion and oxide scale formation of nickel in molten NaOH at various basicity levels.

The corrosion behavior of alloy Ni 201 in molten sodium hydroxide (NaOH) at 600 °C was investigated at varying basicity levels of the molten NaOH. The ability for Ni 201 to form passivating oxides was investigated after immersion tests varying from 70 to 340 h under atmospheres of argon and argon with different partial pressure of water. Morphology and thicknesses of the corrosion products were characterized by Scanning Electron Microscopy (SEM) and crystallography of the corrosion products by X-ray Diffraction (XRD).

Corrosion of a Fassier-Duval Telescopic Nail Causing Pain and Osteolysis: A Case Report.

Case: A 15-year-old girl known with osteogenesis imperfecta presented with left femoral pain. She had been treated with multiple Fassier-Duval intramedullary nails, which were still in situ. Radiographic imaging demonstrated focal osteolysis and periosteal reaction at the telescopic junction of the rod in the distal femur.

The STRYDE limb lengthening nail is susceptible to mechanically assisted crevice corrosion: an analysis of 23 retrieved implants.

Background and purpose - We noted several adverse events in patients in whom the first version of the STRYDE limb-lengthening nail (NuVasive Specialized Orthopaedics, San Diego, CA) had been implanted. Pain, osteolysis, periosteal reactions, and cortical hypertrophy at the nail junction were noted. Here, we present the analysis of 23 retrieved STRYDE implants.