Improving Environmental Stress Cracking Resistance of High-Density Polyethylene Grades by Comonomer Addition and Nanocomposite Approach.

The aim of this paper is to determine the effect of polymer density, correlated to the comonomer content, and nanosilica addition on the mechanical and Environmental Stress Cracking Resistance (ESCR) characteristics of high-density polyethylene (HDPE). In this regard, five HDPE samples with similar Melt Flow Index (MFI) and molar mass but various densities were acquired from a petrochemical plant. Two polymerization reactors work in series and differ only in the amount of 1-buene comonomer fed to the second reactor.

In-situ photo-crosslinkable elastomer based on polyalphaolefin/halloysite nanohybrid.

In this research, new injectable and in situ photocurable elastomeric nanohybrids have been fabricated from polyalphaolefin (PAO) resins and halloysite nanofiller. In this regard, the co-oligomerization of long α-olefin monomers (C6, C8 and C10) with alkenol counterparts was carried out via a simple cationic route to provide OH-functionalized PAOs. The newly formed PAO type copolymer resins as well as halloysite nanoclay were then equipped with photocurable CC bonds containing an acrylate moiety.