Wettability of Sn-3.0Ag-0.5Cu Solder Reinforced with TiO and AlO Nanoparticles at Different Reflow Times.

This study investigated the influence of reinforcing 0.50 wt.% of titanium oxide (TiO) and aluminium oxide (AlO) nanoparticles on the wettability performance of a Sn-3.

Effect of the Sintering Mechanism on the Crystallization Kinetics of Geopolymer-Based Ceramics.

This research aims to study the effects of the sintering mechanism on the crystallization kinetics when the geopolymer is sintered at different temperatures: 200 °C, 400 °C, 600 °C, 800 °C, 1000 °C, and 1200 °C for a 3 h soaking time with a heating rate of 5 °C/min. The geopolymer is made up of kaolin and sodium silicate as the precursor and an alkali activator, respectively. Characterization of the nepheline produced was carried out using XRF to observe the chemical composition of the geopolymer ceramics.

Producing Metal Powder from Machining Chips Using Ball Milling Process: A Review.

In the pursuit of achieving zero emissions, exploring the concept of recycling metal waste from industries and workshops (i.e., waste-free) is essential.

Effects of Multiple Reflow on the Formation of Primary Crystals in Sn-3.5Ag and Solder Joint Strength: Experimental and Finite Element Analysis.

The growth and formation of primary intermetallics formed in Sn-3.5Ag soldered on copper organic solderability preservative (Cu-OSP) and electroless nickel immersion gold (ENIG) surface finish after multiple reflows were systematically investigated. Real-time synchrotron imaging was used to investigate the microstructure, focusing on the in situ growth behavior of primary intermetallics during the solid-liquid-solid interactions.

Effect of Sintering Mechanism towards Crystallization of Geopolymer Ceramic-A Review.

Globally, there is an increasing need for ceramic materials that have a variety of applications in the environment, for precision tools, and for the biomedical, electronics, and environmental industries. However, in order to obtain remarkable mechanical qualities, ceramics have to be manufactured at a high temperature of up to 1600 °C over a long heating period. Furthermore, the conventional approach presents issues with agglomeration, irregular grain growth, and furnace pollution.

Thermal design and zeotropic working fluids mixture selection optimization for a solar waste heat driven combined cooling and power system.

Considering the limitation of fossil fuel resources and their environmental effects, the use of renewable energies is increasing. In the current research, a combined cooling and power production (CCPP) system is investigated, the energy source of which is solar energy. Solar energy absorbs by solar flat plate collectors (SFPC).

Recent Advances in Synthesis of Graphite from Agricultural Bio-Waste Material: A Review.

Graphitic carbon is a valuable material that can be utilized in many fields, such as electronics, energy storage and wastewater filtration. Due to the high demand for commercial graphite, an alternative raw material with lower costs that is environmentally friendly has been explored. Amongst these, an agricultural bio-waste material has become an option due to its highly bioactive properties, such as bioavailability, antioxidant, antimicrobial, in vitro and anti-inflammatory properties.

Preparation of Carbon Nanotubes/Alumina Hybrid-Filled Phenolic Composite with Enhanced Wear Resistance.

Hybrid fillers can be produced via various methods, such as physical mixing and chemical modification. However, there is a limited number of studies on the effect of hybridisation on the mechanical performance of hybrid filler-reinforced polymer composites, especially in the context of wear performance. This study investigated the wear resistance of carbon nanotubes (CNTs)/alumina hybrid-filled phenolic composite, where two hybrid methods were used to produce the CNTs/alumina hybrid filler.

Effect of Isothermal Annealing on Sn Whisker Growth Behavior of Sn0.7Cu0.05Ni Solder Joint.

This paper presents an assessment of the effect of isothermal annealing of Sn whisker growth behavior on the surface of Sn0.7Cu0.05Ni solder joints using the hot-dip soldering technique.

Potential of New Sustainable Green Geopolymer Metal Composite (GGMC) Material as Mould Insert for Rapid Tooling (RT) in Injection Moulding Process.

The investigation of mould inserts in the injection moulding process using metal epoxy composite (MEC) with pure metal filler particles is gaining popularity among researchers. Therefore, to attain zero emissions, the idea of recycling metal waste from industries and workshops must be investigated (waste free) because metal recycling conserves natural resources while requiring less energy to manufacture new products than virgin raw materials would. The utilisation of metal scrap for rapid tooling (RT) in the injection moulding industry is a fascinating and potentially viable approach.

Synthesis of Metakaolin Based Alkali Activated Materials as an Adsorbent at Different NaSiO/NaOH Ratios and Exposing Temperatures for Cu Removal.

Water contamination is a major issue due to industrial releases of hazardous heavy metals. Copper ions are among the most dangerous heavy metals owing to their carcinogenicity and harmful effects on the environment and human health. Adsorption of copper ions using alkali activated materials synthesized through the polycondensation reaction of an alkali source and aluminosilicates is the most promising technique, and has a high adsorption capability owing to a large surface area and pore volume.

Mechanical Performance, Microstructure, and Porosity Evolution of Fly Ash Geopolymer after Ten Years of Curing Age.

This paper elucidates the mechanical performance, microstructure, and porosity evolution of fly ash geopolymer after 10 years of curing age. Given their wide range of applications, understanding the microstructure of geopolymers is critical for their long-term use. The outcome of fly ash geopolymer on mechanical performance and microstructural characteristics was compared between 28 days of curing (FA28D) and after 10 years of curing age (FA10Y) at similar mixing designs.

Solidification/Stabilization Technology for Radioactive Wastes Using Cement: An Appraisal.

Across the world, any activity associated with the nuclear fuel cycle such as nuclear facility operation and decommissioning that produces radioactive materials generates ultramodern civilian radioactive waste, which is quite hazardous to human health and the ecosystem. Therefore, the development of effectual and commanding management is the need of the hour to make certain the sustainability of the nuclear industries. During the management process of waste, its immobilization is one of the key activities conducted with a view to producing a durable waste form which can perform with sustainability for longer time frames.

Computer Simulations of End-Tapering Anchorages of EBR FRP-Strengthened Prestressed Concrete Slabs at Service Conditions.

This article examines numerically the behavior of prestressed reinforced concrete slabs strengthened with externally bonded reinforcement (EBR) consisting of fiber-reinforced polymer (FRP) sheets. The non-linear finite element (FE) program Abaqus is used to model EBR FRP-strengthened prestressed concrete slabs tested previously in four-point bending. After the calibration of the computational models, a parametric study is then conducted to assess the influence of the FRP axial stiffness (thickness and modulus of elasticity) on the interfacial normal and shear stresses.

Near-Infrared (NIR) Silver Sulfide (AgS) Semiconductor Photocatalyst Film for Degradation of Methylene Blue Solution.

A silver sulfide (AgS) semiconductor photocatalyst film has been successfully synthesized using a solution casting method. To produce the photocatalyst films, two types of AgS powder were used: a commercialized and synthesized powder. For the commercialized powder (CF/comAgS), the AgS underwent a rarefaction process to reduce its crystallite size from 52 nm to 10 nm, followed by incorporation into microcrystalline cellulose using a solution casting method under the presence of an alkaline/urea solution.

Effectiveness of Dimple Microtextured Copper Substrate on Performance of Sn-0.7Cu Solder Alloy.

This paper elucidates the influence of dimple-microtextured copper substrate on the performance of Sn-0.7Cu solder alloy. A dimple with a diameter of 50 µm was produced by varying the dimple depth using different laser scanning repetitions, while the dimple spacing was fixed for each sample at 100 µm.

Mechanical Properties of Fly Ash-Based Geopolymer Concrete Incorporation Nylon66 Fiber.

This study was carried out to investigate the effect of the diamond-shaped Interlocking Chain Plastic Bead (ICPB) on fiber-reinforced fly ash-based geopolymer concrete. In this study, geopolymer concrete was produced using fly ash, NaOH, silicate, aggregate, and nylon66 fibers. Characterization of fly ash-based geopolymers (FGP) and fly ash-based geopolymer concrete (FRGPC) included chemical composition via XRF, functional group analysis via FTIR, compressive strength determination, flexural strength, density, slump test, and water absorption.

Influence of Polyformaldehyde Monofilament Fiber on the Engineering Properties of Foamed Concrete.

Foamed concrete is considered a green building material, which is porous in nature. As a result, it poses benefits such as being light in self-weight, and also has excellent thermal insulation properties, environmental safeguards, good fire resistance performance, and low cost. Nevertheless, foamed concrete has several disadvantages such as low strength, a large amount of entrained air, poor toughness, and being a brittle material, all of which has restricted its usage in engineering and building construction.

Geopolymer Ceramic Application: A Review on Mix Design, Properties and Reinforcement Enhancement.

Geopolymers have been intensively explored over the past several decades and considered as green materials and may be synthesised from natural sources and wastes. Global attention has been generated by the use of kaolin and calcined kaolin in the production of ceramics, green cement, and concrete for the construction industry and composite materials. The previous findings on ceramic geopolymer mix design and factors affecting their suitability as green ceramics are reviewed.

Mechanical Performance of Fly Ash Based Geopolymer (FAG) as Road Base Stabilizer.

This study examines the strength development of fly ash-based geopolymer (FAG) as a stabilizer for road base material for pavement construction. In the last decade, there has been a rapid development of conventionally treated bases, such as cement-treated bases. However, a major problem with this kind of application is the shrinkage cracking in cement-treated bases that may result in the reflection cracks on the asphalt pavement surface.

The Significant Effect of Mechanical Treatment on Ceramic Coating for Biomedical Application.

Titanium and its alloys are commonly preferred materials used for biomedical implants. However, these alloys have issues related to corrosion resistance as a result of the aggressive attack of human body fluids. Several researchers have attempted to produce a ceramic coating via physical vapour deposition (PVD).

Interaction of Geopolymer Filler and Alkali Molarity Concentration towards the Fire Properties of Glass-Reinforced Epoxy Composites Fabricated Using Filament Winding Technique.

This paper aims to find out the effect of different weight percentages of geopolymer filler in glass-reinforced epoxy pipe, and which can achieve the best mechanical properties and adhesion between high calcium pozzolanic-based geopolymer matrices. Different weight percentages and molarities of epoxy hardener resin and high calcium pozzolanic-based geopolymer were injected into the glass fiber. By manually winding filaments, composite samples were produced, and they were then allowed to cure at room temperature.

Chemical Distributions of Different Sodium Hydroxide Molarities on Fly Ash/Dolomite-Based Geopolymer.

Geopolymers are an inorganic material in an alkaline environment that is synthesized with alumina-silica gel. The structure of geopolymers consists of an inorganic chain of material and a covalent-bound molecular system. Currently, Ordinary Portland Cement (OPC) has caused carbon dioxide (CO) emissions which causes greenhouse effects.

Geopolymer-Based Artificial Aggregates: A Review on Methods of Producing, Properties, and Improving Techniques.

The depletion of aggregate-related natural resources is the primary concern of all researchers globally. Recent studies emphasize the significance of recycling and reusing various types of natural or by-product material waste from industry as a result of the building industry's rising demand for aggregate as the primary component in concrete production. It has been demonstrated that the geopolymer system has exceptional features, such as high strength, superior durability, and greater resistance to fire exposure, making it a viable alternative to ordinary Portland Cement (OPC) concrete.

Improvements of Flexural Properties and Thermal Performance in Thin Geopolymer Based on Fly Ash and Ladle Furnace Slag Using Borax Decahydrates.

This paper elucidates the influence of borax decahydrate addition on the flexural and thermal properties of 10 mm thin fly ash/ladle furnace slag (FAS) geopolymers. The borax decahydrate (2, 4, 6, and 8 wt.%) was incorporated to produce FAB geopolymers.