H(2) formation by electron irradiation of SBA-15 materials and the effect of Cu(II) grafting.

Measurement of H(2) production from electron irradiation (10 MeV) on SBA-15 materials has shown that adsorbed water is attacked preferentially. Silanol groups are only attacked when they are in the majority with respect to adsorbed water, however they are much less efficient at producing H(2). The comparison between water content before and after electron irradiation and the corresponding H(2) production indicates that water desorption is the main route to adsorbed water loss for SBA-15 materials.