Viscoelastic and structural properties of a phenyl-modified polysiloxane system with a three-dimensional structure.

The relationships between the viscoelastic and structural properties of glass-forming materials with polysiloxane bonds, which serve as network formers, and phenyl groups, which act as network terminators, are examined based on shear viscoelasticity, (29)Si MAS NMR, and GPC measurements during the early stages of the network-forming process. The viscosities of the present samples do not depend on the frequency at temperatures up to 200 degrees C, suggesting that the origin of the viscous flow does not include intermolecular entanglement. According to the results of the strain dependence of the elastic modulus, the bridging-oxygen number, and molecular weight, the present polysiloxane system has a complex structure, or distribution of various-sized molecules composed of a polysiloxane network with various dimensionalities, and furthermore an elementary process of the viscosity is simple flow of these molecules.