Dual hardening steels combine precipitation of both secondary hardening carbides and intermetallic phases in a martensitic matrix. Due to this combination, the carbon content necessary to achieve high hardness levels can be reduced, resulting in a decreased amount of large and embrittling carbides. In this study, the influence of different heat treatments on microstructure evolution and secondary hardness is investigated.