Low temperature synthesis of barium oxynitridosilicates using BaCN and SiO.

Barium oxynitridosilicates, Ba3Si6O12N2 and Ba3Si6O9N4, were obtained from a mixture of BaCN2 and SiO2 at 800 °C, which is several hundred degrees lower than the temperature required in solid state reactions using BaCO3, SiO2 and Si3N4. The low-temperature formation mechanism was investigated by thermogravimetry analysis in conjunction with gas chromatography and mass spectroscopy. The phase ratio between the oxynitridosilicates was controlled by tuning the reaction temperature, duration, and atmosphere.

Ferroelectric BaTaON Crystals Grown in a BaCN Flux.

Perovskite-type oxynitride BaTaON has been attracting attention for its large dielectric constant, which is almost independent of the temperature by measurements on its ceramics. Its dielectric characteristics are attributed to polar nanoregions (PNRs) in the average cubic crystal structure. Polarization saturation to produce a butterfly-like piezoresponse force microscopy (PFM) signal was observed on BaTaON crystals in the present study.

Nitrogen-Rich Manganese Oxynitrides with Enhanced Catalytic Activity in the Oxygen Reduction Reaction.

The catalytic activity of manganese oxynitrides in the oxygen reduction reaction (ORR) was investigated in alkaline solutions to clarify the effect of the incorporated nitrogen atoms on the ORR activity. These oxynitrides, with rock-salt-like structures with different nitrogen contents, were synthesized by reacting MnO, Mn2 O3 , or MnO2 with molten NaNH2 at 240-280 °C. The anion contents and the Mn valence states were determined by combustion analysis, powder X-ray diffraction, and X-ray absorption near-edge structure analysis.

Efficient laser performance of Nd:GdVO4 crystals grown by the floating zone method.

Efficient laser performance is demonstrated with Nd:GdVO4 crystals grown by the floating zone method. With a 2-at. % Nd-doped crystal a slope efficiency of 67% is achieved with pumping at 808 nm.