Uniform large-area surface patterning achieved by metal dewetting for the top-down fabrication of GaN nanowire ensembles.

The dewetting of thin Pt films on different surfaces is investigated as a means to provide the patterning for the top-down fabrication of GaN nanowire ensembles. The transformation from a thin film to an ensemble of nanoislands upon annealing proceeds in good agreement with the void growth model. With increasing annealing duration, the size and shape uniformity of the nanoislands improves.

Axial Growth Characteristics of Optically Active InGaAs Nanowire Heterostructures for Integrated Nanophotonic Devices.

III-V semiconductor nanowire (NW) heterostructures with axial InGaAs active regions hold large potential for diverse on-chip device applications, including site-selectively integrated quantum light sources, NW lasers with high material gain, as well as resonant tunneling diodes and avalanche photodiodes. Despite various promising efforts toward high-quality single or multiple axial InGaAs heterostacks using noncatalytic growth mechanisms, the important roles of facet-dependent shape evolution, crystal defects, and the applicability to more universal growth schemes have remained elusive. Here, we report the growth of optically active InGaAs axial NW heterostructures via completely catalyst-free, selective-area molecular beam epitaxy directly on silicon (Si) using GaAs(Sb) NW arrays as tunable, high-uniformity growth templates and highlight fundamental relationships between structural, morphological, and optical properties of the InGaAs region.