Hydrothermal degradation of a 3Y-TZP translucent dental ceramic: A comparison of numerical predictions with experimental data after 2 years of aging.

Objectives: The purpose of the study was to assess the hydrothermal resistance of a translucent zirconia with two clinical relevant surface textures by means of accelerated tests (LTD) and to compare predicted monoclinic fractions with experimental values measured after two years aging at 37°C.

Methods: Polished (P) and ground (G) specimens were subjected to hydrothermal degradation by exposure to water steam at different temperatures and pressures. The t-m phase transformation was quantified by grazing incidence X-ray diffraction (GIXDR).

Surface roughness and EDS characterization of a Y-TZP dental ceramic treated with the CoJet™ Sand.

Objectives: (1) To determine the surface roughness and material loss of a Y-TZP ceramic before and after tribochemical grit blasting and (2) to characterize the changes in elemental surface composition and the phase transformations after tribochemical treatment.

Methods: Machined bar shaped specimens (Zeno, Wieland) were subdivided into three groups. After grit blasting for 10, 20 and 30s respectively, half of the specimens of each group were ultrasonically cleaned in ethanol for 10min.

Gold coating of non-conductive membranes before matrix-assisted laser desorption/ionization tandem mass spectrometric analysis prevents charging effect.

Acquisition of tandem mass spectra from peptides or other analytes deposited on non-conductive membranes is inhibited on instruments combining matrix-assisted laser desorption/ionization with tandem time-of-flight analyzers (MALDI-TOF/TOF) due to a charging effect. A thin layer of gold renders the membrane conductive. This allows adequate data acquisition on MALDI-TOF/TOF systems.