Effect of Prior Boriding on Microstructure and Mechanical Properties of Nanobainitic X37CrMoV5-1 Hot-Work Tool Steel.

The influence of prior pack boriding on the microstructure and properties of nanobainitised X37CrMoV5-1 hot-work tool steel was investigated in the present work. Pack boriding was conducted at 950 °C for 4 h. Nanobainitising consisted of two-step isothermal quenching at 320 °C for 1 h, followed by annealing at 260 °C for 18 h.

The Effect of Hybrid Treatment Combining Boriding and Nanobainitising on the Tribological and Mechanical Properties of 66SiMnCrMo6-6-4 Bearing Steel.

The effect of a new hybrid heat treatment consisting of pack-boriding and nanobainitising on the microstructure and properties of EN 66SiMnCrMo6-6-4 bearing steel was investigated. The hybrid treatment produces a new high-strength (ca. 1480 MPa) material with a hard boride (ca.

Improving the Properties of Composite Titanium Nitride Layers on the AZ91D Magnesium Alloy Using Hydrothermal Treatment.

Coating magnesium alloys with nitride surface layers is a prospective way of improving their intrinsically poor surface properties; in particular, their tribological and corrosion resistance. These layers are usually produced using PVD methods using magnetron sputtering or arc evaporation. Even though the thus-produced layers significantly increase the wear resistance of the alloys, their effects on corrosion resistance are unsatisfactory because of the poor tightness, characteristic of PVD-produced products.