Effect of ultrasonic surface impact on the microstructural characterization and mechanical properties of 316L austenitic stainless steel.

In the present study, effect of ultrasonic impact treatment (UIT) on the microstructural characterization and mechanical properties of 316L stainless steel (hereinafter referred to as 316L) was investigated experimentally. The fatigue fracture mechanism of 316L before and after UIT was revealed. The experimental results indicated that the martensitic grain size induced at the impact edge was about 2.

Experimental study on pore structure characteristics and thermal conductivity of fibers reinforced foamed concrete.

The pore structure characteristics and thermal conductivity of foamed concrete (FC) reinforced with glass fibers (GF), polyvinyl alcohol fibers (PVAF) and polypropylene fibers (PPF) were investigated experimentally in this article. Firstly, GF, PVAF or PPF with different mass fractions (0%, 1%, 1.5% and 2%) were added to the Portland cement, fly ash and plant protein foaming agent to prepare the FC.