Unveiling the Potential of Redox Chemistry to Form Size-Tunable, High-Index Silicon Particles.

Silicon particles of intermediate sizes (75-200 nm) scatter visible wavelengths, making them promising candidates for optical devices. The solution synthesis of silicon particles in this size range, however, has proved challenging for chemists over the past few decades. Here, a solution-phase synthesis provides a pathway toward reaching size tunability between 45 and 230 nm via changing the reactant ratio in the reaction between a silicon Zintl phase (NaSi) with an amidinate-stabilized Si(IV) coordination complex.

Size-tunable silicon nanoparticles synthesized in solution a redox reaction.

A current challenge in silicon chemistry is to perform liquid-phase synthesis of silicon nanoparticles, which would permit the use of colloidal synthesis techniques to control size and shape. Herein we show how silicon nanoparticles were synthesized at ambient temperature and pressure in organic solvents through a redox reaction. Specifically, a hexacoordinated silicon complex, bis(,'-diisopropylbutylamidinato)dichlorosilane, was reduced by a silicon Zintl phase, sodium silicide (NaSi).

Understanding the Formation Mechanisms of Silicon Particles from the Thermal Disproportionation of Hydrogen Silsesquioxane.

Crystalline silicon particles sustaining Mie resonances are readily obtained from the thermal processing of hydrogen silsesquioxane (HSQ). Here, the mechanisms involved in silicon particle formation and growth from HSQ are investigated through real-time analysis using an environmental transmission electron microscope and X-ray diffractometer. The nucleation of Si nanodomains is observed starting around 1000 °C.