Electrostatic loading and photoredox-based release of molecular cargo from oligoviologen-crosslinked microparticles.

Although on-demand cargo release has been demonstrated in a wide range of microparticle platforms, many existing methods lack specific loading interactions and/or undergo permanent damage to the microparticle to release the cargo. Here, we report a novel method for electrostatically loading negatively charged molecular cargo in oligoviologen-crosslinked microparticles, wherein the cargo can be released upon activation by visible light. A water-in-oil (W/O) emulsion polymerization method was used to fabricate narrowly dispersed microparticles crosslinked by a dicationic viologen-based dimer and a poly(ethylene glycol) diacrylate.

Iterative step-growth synthesis and degradation of unimolecular polyviologens under mild conditions.

An iterative step-growth addition method was used to expedite the gram-scale synthesis of main-chain polyviologens by several days, while also producing the longest main-chain polyviologen (, 26 viologen subunits) reported to date. Facile degradation using inorganic and organic aqueous bases was also demonstrated for a representative oligoviologen (6V-Me·12Cl), a polyviologen (26V-Me·52Cl), and oligoviologen-crosslinked hydrogels.

Dynamic, multimodal hydrogel actuators using porphyrin-based visible light photoredox catalysis in a thermoresponsive polymer network.

Hydrogels that can respond to multiple external stimuli represent the next generation of advanced functional biomaterials. Here, a series of multimodal hydrogels were synthesized that can contract and expand reversibly over several cycles while changing their mechanical properties in response to blue and red light, as well as heat (∼50 °C). The light-responsive behavior was achieved through a photoredox-based mechanism consisting of photoinduced electron transfer from a zinc porphyrin photocatalyst in its excited state to oligoviologen-based macrocrosslinkers, both of which were integrated into the hydrogel polymer network during gel formation.