Aging effect on surface chemistry and sorption properties of atmospheric pressure plasma treated lignocellulosic jute fibers.

Jute fibers are characterized by a heterogeneous chemical composition (cellulose and non-cellulosic components) and a complex layered structure with a hydrophobic surface outer layer responsible for their low wettability. In this work, after the removal of water-soluble components, raw jute fibers were subjected to atmospheric pressure dielectric barrier discharge (DBD) under different conditions (at 150 or 300 Hz) to tailor jute fiber surface structure and wettability. The research was focused on the aging effect during natural aging in a standard atmosphere investigated up to three weeks after DBD treatment.

Films based on TEMPO-oxidized chitosan nanoparticles: Obtaining and potential application as wound dressings.

A series of novel films based on TEMPO-oxidized chitosan nanoparticles were prepared by casting method. Fourier transform infrared spectroscopy (FTIR) was employed to ascertain the chemical structure of TEMPO-oxidized chitosan. The surface morphology of the TEMPO-oxidized chitosan nanoparticles was analyzed by atomic force microscopy (AFM).

Obtaining Medical Textiles Based on Viscose and Chitosan/Zinc Nanoparticles with Improved Antibacterial Properties by Using a Dielectric Barrier Discharge.

This study aimed to obtain functional viscose textiles based on chitosan coatings with improved antibacterial properties and washing durability. For that reason, before functionalization with chitosan/zinc nanoparticles (NCH+Zn), the viscose fabric was modified by nonthermal gas plasma of dielectric barrier discharge (DBD) to introduce into its structure functional groups suitable for attachment of NCH+Zn. NCH+Zn were characterized by measurements of hydrodynamic diameter and zeta potential and AFM.

Chitosan Nanoparticles Functionalized Viscose Fabrics as Potentially Durable Antibacterial Medical Textiles.

This research proposed two pretreatments of viscose fabrics: oxidation with 2,2,6,6-tetramethylpiperidine-1-oxy radical (TEMPO) and coating with TEMPO-oxidized cellulose nanofibrils (TOCN), to introduce functional groups (COOH and CHO) suitable for irreversible binding of chitosan nanoparticles without and with embedded zinc (NCS and NCS + Zn, respectively) and consequently achieving washing durable antibacterial properties of the chitosan nanoparticles functionalized fabrics. The characterizations of pretreated and chitosan nanoparticles functionalized fabrics were performed by FTIR and XPS spectroscopy, elemental analysis, inductively coupled plasma optical emission spectrometry, zeta potential measurements, scanning electron microscopy, determination of COOH and CHO groups content, and antimicrobial activity under dynamic contact conditions. Influence of pretreatments on NCS and NCS + Zn adsorption, chemical, electrokinetic, and antibacterial properties as well as morphology, and washing durability of NCS and NCS + Zn functionalized fabrics were studied and compared.

Influence of Different Pretreatments on the Antibacterial Properties of Chitosan Functionalized Viscose Fabric: TEMPO Oxidation and Coating with TEMPO Oxidized Cellulose Nanofibrils.

The main objective of this study was to obtain chitosan functionalized viscose fabric with improved antibacterial properties and washing durability. In this regard carboxyl and aldehyde groups, as binding points for irreversible chitosan attachment into/onto viscose fabric, were introduced by two different pretreatments: 2,2,6,6-tetramethylpiperidine-1-oxy radical (TEMPO) oxidation and coating with TEMPO oxidized cellulose nanofibrils (TOCN). The Fourier transform infrared spectroscopy, elemental analysis, zeta potential measurements, scanning electron microscopy, breaking strength and antibacterial testing were used to evaluate the influence of these pretreatments on chitosan binding, but also on chemical, electrokinetic, morphological, mechanical and antibacterial properties of pretreated and chitosan functionalized viscose fabrics.