Solid State Processing of BCZT Piezoceramics Using Ultra Low Synthesis and Sintering Temperatures.

Lead-free (BaCa) (Ti Zr) O (BCZT) ceramics were prepared by a solid-state route (SSR) using ultra-low synthesis (700 °C/30 min and 700 °C/2 h) and sintering temperatures (from 1150 °C to 1280 °C), due to prior activation and homogenization by attrition milling of the starting high purity raw materials for 6 h before the synthesis and of the calcined powders for 3 h before the sintering. The comparison of the thermal analysis of the mixture of the starting raw materials and the same mixture after 6 h attrition milling allowed to evidence the mechanisms of activation, resulting in a significant decrease of the perovskite formation temperature (from 854 °C down to 582 °C). The secondary phases that limit the functional properties of the ceramic and their evolution with the sintering conditions were analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM), which allowed the design of a two-step sintering method to eliminate them.

Improving the Photocatalytic Activity of Mesoporous Titania Films through the Formation of WS/TiO Nano-Heterostructures.

Heterostructures formed by anatase nanotitania and bidimensional semiconducting materials are expected to become the next-generation photocatalytic materials with an extended operating range and higher performances. The capability of fabricating optically transparent photocatalytic thin films is also a highly demanded technological issue, and increasing the performances of such devices would significantly impact several applications, from self-cleaning surfaces to photovoltaic systems. To improve the performances of such devices, WS/TiO heterostructures obtained by incorporating two-dimensional transition metal dichalcogenides layers into titania mesoporous ordered thin films have been fabricated.

Processing Optimization and Toxicological Evaluation of "Lead-Free" Piezoceramics: A KNN-Based Case Study.

Due to the ever-increasing limitations of the use of lead-based materials, the manufacturing of lead-free piezoceramics with competitive piezoelectric properties and established nontoxicity is considered a priority for the scientific and industrial community. In this work, a lead-free system based on sodium potassium niobate (KNN), opportunely modified with MgNbO (MN), was prepared through a combination of a mechanochemical activation method and air sintering, and its toxicity was evaluated. The effect of the mechanical processing on the microstructure refinement of the processed powders was established by X-ray diffraction and the average crystallite size content of the NbO species was evaluated.