Possibilities of Increasing the Durability of Dies Used in the Extrusion Process of Valve Forgings from Chrome-Nickel Steel by Using Alternative Materials from Hot-Work Tool Steels.

This study refers to an analysis of the dies used in the first operation of producing a valve forging from chromium-nickel steel NC3015. The analyzed process of manufacturing forgings of exhaust valves is realized in the co-extrusion technology, followed by forging in closed dies. This type of technology is difficult to master, mainly due to the increased adhesion of the charge material to the tool substrate as well as the complex conditions of the tools' operations, which are caused by the cyclic thermo-mechanical loads and also the hard tribological conditions.

Metallographic Evaluation of Increased Susceptibility to Intermediate Embrittlement of Engine Valve Forgings Made of NCF 3015 High Nickel and Chromium Steel.

This paper focused on determining the increased tendency of cracking after the die forging process of high nickel and chromium steel. The increase in carbon content in austenitic nickel-chromium steel promoted the tendency of valve forgings to forging intergranular crack on the valve head. Attention was paid to issues related to the chemical composition of the material to be considered when hot forming nickel-chromium steel components.

Comparative Analysis of the Wear of NC11LV and Hardox 600 Steel Used in Tools for Extrusion of Clay Strands in the Process of Producing Ceramic Roof Tiles.

This article presents the results of a comparative analysis performed with respect to the wear of tools used for the extrusion of a clay strand (for ceramic roof tile) made from two materials: steel NC11LV and steel Hardox 600. The aim of the studies was to determine the causes and mechanisms of wear as well as to evaluate the possibility of choosing the optimal material, mostly in respect to its resistance to intensive wear as well as an increase in the operation time. The results of the conducted investigations included: an analysis of the technology, thermovision measurements of the forming process, a macroscopic analysis combined with 3D scanning of the worn tools, ball-on-disc tests of the sliding wear resistance and hardness measurements.

Influence of Corrosion on Fatigue of the Fastening Bolts.

The aim of the present work was to evaluate high-strength bolt corrosion fatigue based on metallographic examinations. The conducted tests were focused on the analysis of damaged martensitic bolts. It was found that the combined presence of cyclic loads and a corrosive environment was the cause of the accelerated fatigue of the fastening bolts.

Preliminary Studies of the Durability of Tools Used to Form Ceramic Tiles Made of Hardox 600 and NC11LV Steel.

The study performs a comparative analysis of the wear of tools made of two wear-resistant materials: steel Hardox 600 and NC11LV, used in the process of forming a band for roofing tiles. The analyses were to allow the assessment of the possibility of replacing the standard material for tools in this process with a much less expensive tool steel for cold work after heat treatment (with a large number of carbides), as an alternative material dedicated to tools resistant to intense abrasive wear. The performed investigations included a macroscopic and geometrical analysis with the use of 3D scanning, microstructural analyses conducted by means of a light microscope, as well as an analysis of the topography of the working areas of the tools with the use of SEM, and microhardness tests.

Effect of Cooling Rate at the Eutectoid Transformation Temperature on the Corrosion Resistance of Zn-4Al Alloy.

The main purpose of this work was to experimentally determine the effect of the cooling rate during the eutectoid transformation on the corrosion resistance of a hypoeutectic Zn-4Al cast alloy in 5% NaCl solution. This was considered in relation to the alloy microstructure. For this purpose, metallographic and electrochemical studies were performed.