Influence of diatomite and its base modifications on the self-adhesive properties of silicone pressure-sensitive adhesives.

The study examined how diatomite and its modifications affected the self-adhesive ability of silicone pressure-sensitive adhesives. To create adhesive composition for testing, fillers were added to a commercial silicone resin, which were then used to create new modified pressure-sensitive tapes. The resulting tapes were tested to determine their adhesion, tack, cohesion at room and elevated temperature, SAFT test (Shear Adhesive Failure Temperature), pot-life (viscosity) and shrinkage.

Influence of Illite and Its Amine Modifications on the Self-Adhesive Properties of Silicone Pressure-Sensitive Adhesives.

Obtaining new silicone self-adhesive in the presence of modified illite has been described. The filler was modified with N,N,4-trimethylaniline. The effect of illite content and modification on functional properties (adhesion, cohesion, stickiness, and shrinkage) was determined.

Influence of Acid-Modified Clinoptilolite on the Self-Adhesive Properties of Silicone Pressure-Sensitive Adhesives.

The preparation of a new "eternally alive adhesive" based on silicone pressure-sensitive adhesives with clinoptilolite is presented. Neat and acid-modified (i.e.