Effect of multiple adduct fullerenes on microstructure and phase behavior of P3HT:fullerene blend films for organic solar cells.

The bis and tris adducts of [6,6]phenyl-C(61)-butyric acid methyl ester (PCBM) offer lower reduction potentials than PCBM and are therefore expected to offer larger open-circuit voltages and more efficient energy conversion when blended with conjugated polymers in photovoltaic devices in place of PCBM. However, poor photovoltaic device performances are commonly observed when PCBM is replaced with higher-adduct fullerenes. In this work, we use transmission electron microscopy (TEM), steady-state and ultrafast time-resolved photoluminescence spectroscopy (PL), and differential scanning calorimetry (DSC) to probe the microstructural properties of blend films of poly(3-hexylthiophene-2,5-diyl) (P3HT) with the bis and tris adducts of PCBM.

Competition between the charge transfer state and the singlet states of donor or acceptor limiting the efficiency in polymer:fullerene solar cells.

We study the appearance and energy of the charge transfer (CT) state using measurements of electroluminescence (EL) and photoluminescence (PL) in blend films of high-performance polymers with fullerene acceptors. EL spectroscopy provides a direct probe of the energy of the interfacial states without the need to rely on the LUMO and HOMO energies as estimated in pristine materials. For each polymer, we use different fullerenes with varying LUMO levels as electron acceptors, in order to vary the energy of the CT state relative to the blend with [6,6]-phenyl C61-butyric acid methyl ester (PCBM).