Elucidation of the variability in consistency of pharmacopoeia quality petrolatum.

The Pharmacopeia monograph for petrolatum poorly defines the material's physical properties. Indeed, differences between petrolatum grades can be substantial; yield stress varies between 65 and 280 Pa which can be compared with the consistency of respectively thin cream or thick ointment. This variation is not only due to differences in composition or refining process but also as a result of different processing; for example, thermal history influences petrolatum structure considerably.

Carbon-supported base metal nanoparticles: cellulose at work.

Pyrolysis of base metal salt loaded microcrystalline cellulose spheres gives a facile access to carbon-supported base metal nanoparticles, which have been characterized with temperature-dependent XRD, SEM, TEM, ICP-MS and elemental analysis. The role of cellulose is multifaceted: 1) it facilitates a homogeneous impregnation of the aqueous base metal salt solutions, 2) it acts as an efficacious (carbonaceous) support material for the uniformly dispersed base metal salts, their oxides and the metal nanoparticles derived therefrom, and 3) it contributes as a reducing agent via carbothermal reduction for the conversion of the metal oxide nanoparticles into the metal nanoparticles. Finally, the base metal nanoparticles capable of forming metastable metal carbides catalytically convert the carbonaceous support into a mesoporous graphitic carbon material.

Release behavior and intra-articular biocompatibility of celecoxib-loaded acetyl-capped PCLA-PEG-PCLA thermogels.

In this study, we investigated the in vitro and in vivo properties and performance of a celecoxib-loaded hydrogel based on a fully acetyl-capped PCLA-PEG-PCLA triblock copolymer. Blends of different compositions of celocoxib, a drug used for pain management in osteoarthritis, and the acetyl-capped PCLA-PEG-PCLA triblock copolymer were mixed with buffer to yield temperature-responsive gelling systems. These systems containing up to 50 mg celecoxib/g gel, were sols at room temperature and converted into immobile gels at 37 °C.

Effect of polymer composition on rheological and degradation properties of temperature-responsive gelling systems composed of acyl-capped PCLA-PEG-PCLA.

In this study, the ability to modulate the rheological and degradation properties of temperature-responsive gelling systems composed of acyl-capped poly(ε-caprolactone-co-lactide)-b-poly(ethylene glycol)-b-poly(ε-caprolactone-co-lactide) (PCLA-PEG-PCLA) triblock copolymers was investigated. Eight polymers with varying molecular weight of PCLA, caproyl/lactoyl ratio (CL/LA) and capped with either acetyl- or propionyl-groups were synthesized by ring-opening polymerization of L-lactide and ε-caprolactone in toluene using PEG as initiator and tin(II) 2-ethylhexanoate as catalyst, and subsequently reacted in solution with an excess of acyl chloride to yield fully acyl-capped PCLA-PEG-PCLA. The microstructure of the polymers was determined by (1)H NMR, and the thermal properties and crystallinity of the polymers in dry state and in 25 wt % aqueous systems were studied by differential scanning calorimetry and X-ray diffraction.

Extended structure design with simple molybdenum oxide building blocks and urea as a directing agent.

We report here a simple one-pot directed synthesis of an oxomolybdate urea composite in which elementary molybdenum oxide building blocks are linked together with the aid of urea. This type of directed material design resulted in large rod-like crystals of an inorganic-organic hybrid extended structure of {MoO 3(NH 2-CO-NH 2)} infinity consisting of right- and left-handed helical units. In the crystal structure urea acts both as a glue that links the inorganic molybdenum units into a helix and as a supramolecular linker for the stabilization of the crystal structure as a whole.