Structural characterization and mechanical properties of wet-processed fibreboard based on chemo-thermomechanical pulp, furanic resin and cellulose nanocrystals.

Fibreboards are made of lignocellulosic fibres and synthetic adhesive which connect them. These synthetic adhesives, while relatively low-cost, are usually non-biodegradable and may cause health and environmental issues. Therefore, in recent years, there has been an increased demand for replacing these adhesives with bio-derived adhesives.

Cellulose-nanofiber/polygalacturonic acid coatings with high oxygen barrier and targeted release properties.

A bio-inspired coating consisting of pectin (polygalacturonic acid) and cationic cellulose nanofibers were successfully produced by the layer-by-layer method. The build-up and the morphology of the resulting coatings were studied with spectroscopic ellipsometry and atomic force microscopy, respectively. The coating was able to survive the exposure of a simulated gastric fluid, but was partially degraded upon exposure to pectinase enzyme, which simulate the action of the microbial symbionts present in the human colon.

Cellulose nanopaper structures of high toughness.

Cellulose nanofibrils offer interesting potential as a native fibrous constituent of mechanical performance exceeding the plant fibers in current use for commercial products. In the present study, wood nanofibrils are used to prepare porous cellulose nanopaper of remarkably high toughness. Nanopapers of different porosities and from nanofibrils of different molar mass are prepared.

A high strength nanocomposite based on microcrystalline cellulose and polyurethane.

A high-strength elastomeric nanocomposite has successfully been prepared by dispersing microcrystalline cellulose in a polyurethane matrix. The resulting nanocomposites show increased strain-to-failure in addition to increased stiffness and strength compared to the unfilled polyurethane. The optimal composite contained 5 wt % cellulose.