Synthesis of high concentration colloid solution of silica-coated AgI nanoparticles.

Methods for high concentration silica-coated silver iodide (AgI/SiO2) particles, which could be practically used as X-ray contrast agent, were examined. The first was a single-step method, which was to prepare AgI nanoparticles at an AgI concentration of 5 x 10(-3) M and coat the AgI nanoparticles with silica shell by a Stöber method. The second was a multiple-step method, which was to repeat a step for preparing a AgI/SiO2 particle colloid solution with 10(-3) M AgI 5 times for adjusting a final AgI concentration to 5 x 10(-3) M.

Synthesis of silica-coated AgI nanoparticles and immobilization of proteins on them.

This paper describes a method for preparing silica-coated silver iodide (AgI/SiO2) particles and immobilizing proteins on the AgI/SiO2 particles. Colloid solution of AgI particles was prepared by mixing AgClO4 aqueous solution and KI aqueous solution. Silica-coating of the AgI particles was performed by adding 3-mercaptopropyltrimethoxysilane, tetraethylorthosilicate/ethanol solution and NaOH aqueous solution successively to the AgI colloid solution.